% sputtering yield : C -> C
% z1= 6, m1= 12.01, z2= 6, m2= 12.01, sbe=7.41 eV, rho=1.85 g/cm**3
% ef=7.35 eV, esb=7.41 eV, kk0=kk0r=2, kdee1=kdee2=3, ipot=ipotr=1 (KrC)
% ca=1.00
% program : trvmc, testvmcx
% ne=19, na= 9
%
%  e0     0      15      30      45      55      65      75      80      85
%
    8                                          5.00e-6 7.69e-6 8.99e-6 9.65e-6
   10                  5.00e-7 6.50e-6 2.07e-5 2.60e-5 3.81e-5 3.87e-5 3.78e-5
   12                  3.21e-6 2.36e-5 5.03e-5 7.39e-5 8.42e-5 8.64e-5 8.58e-5
   15                  1.10e-5 8.90e-5 1.47e-4 2.00e-4 2.36e-4 2.60e-4 2.64e-4
   17                                          3.95e-4
   20          1.00e-5 8.10e-5 3.60e-4 6.74e-4 1.18e-3 1.73e-3 1.95e-3 2.05e-3
   25  5.00e-6 3.10e-5 2.76e-4 1.28e-3 2.90e-3 5.02e-3 6.61e-3 7.13e-3 7.12e-3
   30  1.83e-5 1.00e-4 8.15e-4 3.95e-3 8.02e-3 1.31e-2 1.55e-2 1.55e-2 1.60e-2  
   40  1.35e-4 5.96e-4 3.73e-3 1.56e-2 2.85e-2 4.06e-2 4.16e-2 3.40e-2 3.85e-2
   45  2.74e-4
   50  5.21e-4 1.89e-3 1.04e-2 3.58e-2 5.81e-2 7.50e-2 7.57e-2 7.03e-2 6.37e-2 
   70  2.57e-3 7.31e-3 3.01e-2 8.40e-2 1.34e-1 1.63e-1 1.51e-1 1.28e-1 1.10e-1
  100  8.84e-3 1.96e-2 6.53e-2 1.66e-1 2.45e-1 2.89e-1 2.45e-1 1.99e-1 1.54e-1 
  140  2.13e-2 3.95e-2 1.11e-1 2.52e-1 3.74e-1 4.43e-1 3.65e-1 2.60e-1 1.83e-1
  200  4.14e-2 6.76e-2 1.63e-1 3.49e-1 5.16e-1 6.33e-1 5.14e-1 3.53e-1 2.11e-1  
  300  7.16e-2 1.06e-1 2.27e-1 4.60e-1 6.83e-1 8.63e-1 7.42e-1 4.94e-1 2.42e-1
  500  1.16e-1 1.61e-1 3.05e-1 5.98e-1 8.91e-1 1.18e-0 1.15e-0 7.92e-1 3.01e-1 
 1000  1.78e-1 2.28e-1 3.93e-1 7.38e-1 1.10e-0 1.55e-0 1.77e-0 1.45e-0 4.92e-1
 1200  2.13E-1