# sputtering yield : Li -> Li # z1= 3, m1= 6.94, z2= 3, m2= 6.94, Es=1.68 eV, rho=0.53 g/cm**3 # ef=1.18, esb=1.68, kk0=kk0r=2, kdee1=kdee2=3, ipot=ipotr=1 (KrC) # program: newtrim (Laszlo), IPP 9/82 # ne= 9, na=10 # # e0 0 30 45 55 60 65 70 75 80 85 # 20 5.42e-3 2.28e-1 50 4.29e-2 5.96e-1 100 9.48e-2 2.60e-1 5.19e-1 9.21e-1 1.05e-0 1.13e-0 1.07e-0 7.68e-1 3.21e-1 200 1.50e-1 3.43e-1 6.56e-1 1.18e-0 1.39e-0 1.58e-0 1.62e-0 1.36e-0 5.19e-1 500 1.91e-1 2.29e-0 1000 2.07e-1 3.75e-1 6.57e-1 1.04e-0 1.33e-0 2.06e-0 2.49e-0 2.82e-0 2.16e-0 2000 1.87e-1 2.38e-0 5000 1.44e-1 2.01e-0 10000 1.19e-1 1.48e-0