# sputtered energy : He -> W # z1= 2, m1= 4.00, z2=74, m2=183.85, esb=8.68 eV, rho=19.29 g/cm**3 # ef=0.20 eV, esb=0.00 eV, ca=1.00, kk0=kk0r=2, kdee1=kdee2=3, ipot=ipotr=1 (KrC) # program: trvmc # ne=20, na=9 # # e0 0 15 30 45 55 65 75 80 85 # 125 2.08e-8 2.68e-8 3.18e-8 3.61e-8 3.06e-8 1.40e-8 6.54e-9 130 1.27e-7 1.51e-7 1.51e-7 1.44e-7 1.30e-7 6.83e-8 1.25e-8 140 8.49e-7 8.78e-7 9.35e-7 9.63e-7 7.76e-7 4.76e-7 1.17e-7 2.09e-8 150 2.53e-6 2.69e-6 2.71e-6 2.69e-6 2.49e-6 1.69e-6 4.74e-7 9.04e-8 170 1.03E-5 1.02E-5 1.10E-5 1.14E-5 9.98E-6 6.82E-6 2.45E-6 6.30E-7 200 3.17E-5 3.35E-5 3.46E-5 3.71E-5 3.17E-5 2.65E-5 1.05E-5 3.05E-6 3.11E-8 250 8.64E-5 8.36E-5 9.33E-5 1.01E-4 9.90E-4 8.17E-5 4.18E-5 1.47E-5 2.45E-7 300 1.46E-4 1.48E-4 1.62E-4 1.81E-4 1.79E-4 1.68E-4 1.02E-4 4.41E-5 1.34E-6 350 2.10E-4 2.03E-4 2.28E-4 2.49E-4 2.68E-4 2.66E-4 1.89E-4 1.07E-4 4.68E-6 400 2.53E-4 2.60E-4 2.83E-4 3.31E-4 3.59E-4 3.80E-4 3.31E-4 1.86E-4 1.18E-5 500 3.46E-4 3.57E-4 3.96E-4 4.49E-4 5.08E-4 5.92E-4 6.19E-4 4.61E-4 4.58E-5 600 3.96E-4 4.24E-4 4.75E-4 5.52E-4 6.34E-4 7.82E-4 9.41E-4 8.11E-4 1.15E-4 700 4.56E-4 4.81E-4 5.28E-4 6.20E-4 7.35E-4 9.48E-4 1.20E-3 1.15E-3 2.15E-4 1000 5.38E-4 5.61E-4 6.15E-4 7.64E-4 9.64E-4 1.29E-3 1.86E-3 1.91E-3 5.80E-4 1400 5.63E-4 5.80E-4 6.50E-4 8.57E-4 1.09E-3 1.52E-3 2.27E-3 2.50E-3 1.10E-3 2000 5.35E-4 5.54E-4 6.44E-4 8.32E-4 1.11E-3 1.60E-3 2.42E-3 2.82E-3 1.70E-3 5000 3.57E-4 3.77E-4 4.47E-4 6.34E-4 8.76E-4 1.25E-3 2.00E-3 2.57E-3 2.55E-3 10000 2.09E-4 2.32E-4 2.88E-4 4.06E-4 5.61E-4 8.55E-4 1.45E-3 1.90E-3 2.34E-3 20000 1.04E-4 1.19E-4 1.56E-4 2.26E-4 3.15E-4 4.89E-4 8.64E-4 1.23E-3 1.73E-3 50000 3.28E-5 3.71E-5 5.19E-5 8.46E-5 1.25E-4 1.86E-4 3.60E-4 5.48E-4 9.08E-4